Image of Penentuan tebal dinding tangki reaktor kartini menggunakan metode ultrasonic testing

Tugas Akhir

Penentuan tebal dinding tangki reaktor kartini menggunakan metode ultrasonic testing

Penentuan Tebal Dinding Tangki Reaktor Kartini Menggunakan Metode Ultrasonic Testing. Reaktor Kartini merupakan salah satu reaktor nuklir jenis TRIGA MARK II yang memiliki 2 struktur penting di dalamnya, yaitu perisai dan tangki reaktor. Tangki reaktor memiliki fungsi sebagai wadah dari berbagai komponen reaktor. Dikarenakan pentingnya fungsi dari tangki reaktor, maka dinding tangki reaktor harus dilakukan pemeriksaan secara berkala. Namun pada kenyataannya, dinding tangki Reaktor Kartini dilakukan pengukuran terakhir tahun 2002. Pada penelitian ini dilakukan pemeriksaan terhadap ketebalan dinding tangki Reaktor Kartini dengan menggunakan metode Ultrasonic Testing teknik immersion untuk mengetahui tingkat kelayakan, dan sisa umur tangki. Pengukuran dilakukan menggunakan Ultrasonic UltraScan 5 menggunakan orde 25×25 cm Dari pemeriksaan yang dilakukan, diperoleh hasil bahwa Reaktor Kartini masih layak digunakan karena memenuhi standar minimum ketebalan. Laju korosi pada dinding tangki Reaktor Kartini berkisar 0,0205 mm/tahun sampai 0,0250 mm/tahun. Berdasarkan laju korosinya, dapat diperkirakan sisa umur tangki Reaktor Kartini yaitu sekitar 21 tahun.rnKata Kunci: Tangki Reaktor, Ultrasonic Testing, Immersion, Ketebalan, Laju KorosirnrnABSTRACTrnThickness Determination Of The Kartini Reactor Tank Wall Using Ultrasonic Testing Method. Kartini Reactor is one of the TRIGA MARK II nuclear reactors, which have 2 important structures, the shield and the reactor tank. The reactor tank has a function as a container of various reactor components. Due to the importance of the function of the reactor tank, the wall tank reactor must be checked periodically. In this study, an inspection of the thickness of the Kartini Reactor wall tank using the Ultrasonic Testing technique immersion was examined to find out the feasibility level and the remaining age of the tank. The inspection is carried out using Ultrasonic UltraScan 5 with a distance between the inspection points is 25 cm From this inspection, the result was obtained that the Kartini Reactor was still good to use because it qualifies the minimum standard thickness from General Atomic. The corrosion rate on the Reactor Kartini wall tank ranges from 0,0205 mm/year to 0.0250 mm/year. Based on the corrosion rate, it can be estimated that the remaining age of the Kartini Reactor tank is around 21 years.rnKeywords: Reactor Tank, Ultrasonic Testing, Immersion, Thickness, Corrosion Ratern rn rn

Ketersediaan
S19-02369/TA/M/19 621.039.53(043) ALF pPerpustakaan Poltek Nuklir (600)Tersedia
Informasi Detail
Judul Seri
-
No. Panggil
621.039.53(043) ALF p
Penerbit
Yogyakarta : STTN-BATAN.,
Deskripsi Fisik
xv, 53 halaman : ilustrasi ; 30 cm
Bahasa
Indonesia
ISBN/ISSN
-
Klasifikasi
621.039.53(043)
Tipe Isi
teks
Tipe Media
tanpa perantara
Tipe Pembawa
volume
Edisi
-
Subjek
Reactor Components
Info Detail Spesifik
-
Pernyataan Tanggungjawab
Versi lain/terkait

Tidak tersedia versi lain

Lampiran Berkas
Komentar
Anda harus login sebelum memberikan komentar