Peningkatan konduktivitas dan kapasitas ionogel berbasis kappa Karagenan-PVA dengan penembahan filler silika dan pori

Ionogel berbasil polyvinyl alkohol (PVA) grafting kappa karagenan telah berhasil disintesis. 1Ethylpyridinium tetrafluoro-borate sebagai larutan ionik. Silika hasil ekstraksi fly ash sebagai filler dan kalsium karbonat (CaCO3) sebagai bahan porogen ditambahkan ke dalam larutan PVA/kappa karagenan. Hasil analisis FTIR ditemukan silika dalam grafting PVA/kappa karagenan dalam bentuk ikatan Si-OH dan Si-C. Hasil analisis XRD menunjukkan penambahan filler silika dapat menurunkan derajat kristalinitas. Hasil menunjukkan fraksi gel menurun dengan penambahan silika dan meningkat dengan penambahan CaCO3. Densitas meningkat dengan peningkatan silika dan menurun dengan peningkatan CaCO3. Proses swelling di dalam air telah dilakukan dan diperoleh hasil bahwa derajat swelling meningkat dan kemudian turun dengan penambahan filler silika, tetapi tetap meningkat dengan peningkatan CaCO3. konduktivitas dan kapasitansi meningkat dengan peningkatan silika dan CaCO3. konduktivitas dan kapasitansi tertinggi pada ionogel mengandung CaCO3 1,5% dengan kapasitansi dan konduktivitas yakni 1,008 mF/g dan 4,164 x 10-6 S/cm
Kata kunci: Ionogel, Kapasitansi Konduktivitas, Filler Silika, Pori.

An ionogel was successfully synthesized on the basis of polyvinyl alcohol (PVA) grafted kappa carrageenan. 1Ethylpyridinium tetrafluoro-borate as a ionic solution. Silica from fly ash extraction as filler and calcium carbonat (CaCO3) as porogen was then added into the PVA/kappa carragenan solution. By analyzing their FTIR spectra, it was found silica on grafted PVA/kappa carrageenan. X-ray diffraction analysis showed that the crystalline was reduced through silica fillers added. The result showed that gel fraction decrease with increasing silica added and increase with increasing CaCO3 added. Density increase with increasing silica added and decrease with increasing CaCO3 added. Water swelling were conducted and the results showed that swelling degree increased first and then decreased with increasing silica added, but keep increase with increasing CaCO3 added. conductivity and capacitance increase with increasing silica and CaCO3.The highest conductivity and capacitance were given by ionogel with CaCO3 1.5%. The Conductivity was 4.164 x 10-6 S/cm and the capacitance was 1.008 mF/g.
Keyword: Ionogel, Capacitance, Conductivity, Silica Filler, Porous.

Ketersediaan
S17-908222/TA/H/17 537.311 UMM pPerpustakaan Poltek NuklirTersedia
Informasi Detail
Judul Seri
-
No. Panggil
537.311 UMM p
Penerbit
Yogyakarta : STTN-BATAN.,
Deskripsi Fisik
x, 82 halaman : ilustrasi ; 30 cm
Bahasa
Indonesia
ISBN/ISSN
-
Klasifikasi
537.311
Tipe Isi
teks
Tipe Media
tanpa perantara
Tipe Pembawa
volume
Edisi
-
Subjek
-
Info Detail Spesifik
-
Pernyataan Tanggungjawab
Versi lain/terkait

Tidak tersedia versi lain

Lampiran Berkas
Komentar
Anda harus login sebelum memberikan komentar