Image of Peningkatan kemampuan fotokatalitik film tipis sputtered titanium dioksida (TiO₂) terdoping silver (Ag) yang diperoleh dengan radiolysis reduction

Tugas Akhir

Peningkatan kemampuan fotokatalitik film tipis sputtered titanium dioksida (TiO₂) terdoping silver (Ag) yang diperoleh dengan radiolysis reduction

Titanium dioksida (TiO2) merupakan semikonduktor yang banyak digunakan sebagai material fotokatalitik yang ramah lingkungan untuk mendegradasi polutan dari gas dan cairan. Dalam penelitian ini disintesis film tipis TiO2 dengan metode DC sputtering pada substrat stainless steel. Film tipis ini kemudian di doping dengan monometallic silver (Ag) menggunakan metode reduksi radiolisis untuk meningkatkan aktivitas fotokatalitiknya. Sintesis TiO2 dan doping dengan Ag berhasil dilakukan yang ditunjukkan oleh hasil karakterisasi SEM-EDS. Dari data SEM-EDS terlihat adanya Ag nanopartikel pada permukaan TiO2 sebanyak 4,34 %wt pada dosis iradiasi 20 kGy. Aktivitas fotokatalik diuji dibawah lampu UV dan sinar matahari. Metilen biru digunakan sebagai model polutan air yang diujikan. Data eksperimen menunjukkan bahwa aktivitas fotokatalitik TiO2 dengan modifikasi Ag mampu mendegradasi lebih baik pada cahaya UV maupun cahaya matahari. Hasil optimum degradasi TiO2 saja pada cahaya UV adalah 28,80% dan dengan doping Ag menjadi 88,44% yang dicapai saat dosis iradiasi precursor Ag 20 kGy. Sedangkan proses degradasi pada cahaya matahari menggunakan TiO2 saja adalah 14,08% dan dengan doping Ag menjadi 59,80% yang juga dicapai saat dosis iradiasi precursor Ag 20 kGy.
Kata kunci: DC Sputtering, reduksi radiolisis, Ag, fotokatalitik.

Titanium dioxide is a semiconductor that is widely used as a eco-friendly photocatalytic material to degrade gas and liquid pollutans. In this research thin film TiO2 is synthesized by DC Sputtering on stainless steel substrate. The thin film is then doped withh monometallic silver by radiolysis reduction to enhance its photocatalytic activity. The synthesize of TiO2 thin film and doping of Ag was succestainless steelfully performed as shown in SEM-EDS characterization result. From SEM-EDS data we can see Ag nanoparticle on TiO2 surface as much as 4,34% wt at 20 kGy irradiation dose. Photocatalytic activity was tested under UV light and sunlight. Methylene blue is used as a water pollutan model to be tested. The experimental data showed that the photocatalytic activity of TiO2 modified Ag is able to degrade better in both UV and sunlight. The optimum result of TiO2 degradation in UV light is as much as 28,8% and with Ag doping is as much as 88,44% achieved at 20 kGy irradiation dosage. While the processof degradation in sunlight using TiO2 is as much as 14,08% and with Ag doping is as much as 59,80% also achieved at 20 kGy irradiation dosage.
Keywords: DC Sputtering, radiolysis reduction, Ag, photocatalytic.

Ketersediaan
S18-013710/TA/H/18 615.849(043) NIS pPerpustakaan Poltek NuklirTersedia
Informasi Detail
Judul Seri
-
No. Panggil
615.849(043) NIS p
Penerbit
Yogyakarta : STTN-BATAN.,
Deskripsi Fisik
xiv, 57 halaman : ilustrasi ; 30 cm
Bahasa
Indonesia
ISBN/ISSN
-
Klasifikasi
615.849(043)
Tipe Isi
teks
Tipe Media
tanpa perantara
Tipe Pembawa
volume
Edisi
-
Subjek
-
Info Detail Spesifik
-
Pernyataan Tanggungjawab
Versi lain/terkait

Tidak tersedia versi lain

Lampiran Berkas
Komentar
Anda harus login sebelum memberikan komentar