Tugas Akhir

Analisis perubahan kualitas disc brake tipe-x hasil nitridasi plasma menggukanan uji mekanik dan kimia

---

Analisis Perubahan Kualitas Disc Brake Tipe-X Hasil Nitridasi Plasma Menggunakan Uji Mekanik Dan Kimia. Telah dilakukan analisis perubahan kualitas disc brake hasil nitridasi plasma. Disc brake merupakan komponen penunjang keselamatan pada kendaraan. Kerusakan pada disc brake dibebabkan adanya deformasi akibat keausan. Laju keausan berbanding terbalik dengan kekerasan maka dilakukan perlakuan kekerasan dngan nitridasi plasma untuk meningkatkan kekerasan. Nitridasi plasma dilakukan dengan parameter nitridasi dengan komposisi campuran gas nitrogen terhadap argon adalah 100:0, 90:10, 80:20, 70:30, dan 60:40 serta waktu post treatment 10, 20, 30, 40, dan 50 menit. Analisis difokuskan pada sifat kekerasan, korosi, dan struktur mikro. Nilai kekerasan maksimum terjadi pada komposisi campuran gas dengan perbandingan 90:10 sebesar 252,72 VHN, dan post treatment pada waktu 20 menit sebesar 223,24 VHN. Nilai laju korosi terkecil sebesar 0,407431 mpy dengan perbandingan gas nitrogen terhadap argon 100:0. Berdasarkan uji SEM-EDS terdapat lapisan keras hasil nitridasi pada permukaan yang dibuktikan adanya perubahan struktur dan unsur pada permukaan. rn rnKata kunci : disc brake, nitridasi plasma, post treatment, komposisi campuran gas rnrnABSTRACT rnQuality Change Analysis Of Disc Brake Type-X With Plasma Nitridation Using Mechanical And Chemical Test. Analysis of changes in disc brake quality of plasma nitriding results has been carried out.. Damage to the disc brake is caused by deformation due to wear. The rate of wear is inversely proportional to hardness, so the treatment of hardness with plasma nitriding is done to increase hardness. Plasma nitriding is done by nitriding parameters with the composition nitrogen toward argon composition by 100:0, 90:10, 80:20, 70:30 and 60:40 argon post treatment duration by 10, 20, 30, 40 and 50 minutes. The analysis focused on the properties of hardness, corrosion, and microstructure. Maksimum hardness with composition gas achieve with compositon 90:10 the hardness value obtain is 252,72 VHN, and using post tretment achieve maxsimum hardness number in 20 minutes with 223,24 VHN. The lowest corrosion rate achieve with 0,407431 mpy using nitridation with 100% nitrogen gas. Based on SEM-EDS test, there is a hard layer of nitriding on the surface which is proven by changes in structure and elements on the surface. rn rnKeyword: disc brake, plasma nitridation, post treatment, gas composition

---

Ketersediaan

S18-0217

7/TA/M/18 614:539.12(043) TEG a

Perpustakaan Poltek Nuklir

Tersedia

Informasi Detail

Judul Seri

-

No. Panggil

614:539.12(043) TEG a

Penerbit

Yogyakarta : STTN-BATAN., 2018

Deskripsi Fisik

xiv, 57 halaman : ilustrasi ; 30 cm

Bahasa

Indonesia

ISBN/ISSN

-

Klasifikasi

614:539.12(043)

Tipe Isi

teks

Tipe Media

tanpa perantara

Tipe Pembawa

volume

Edisi

-

Subjek

-

Info Detail Spesifik

-

Pernyataan Tanggungjawab

Teguh Wiyono

Versi lain/terkait

Lampiran Berkas

Komentar

---

Anda harus login sebelum memberikan komentar