Analisis sifat keras dan komposisi baja karbon rendah hasil perlakuan nitridasi plasma dan pelapisan diamond like carbon

INTISARI ANALISIS SIFAT KERAS DAN KOMPOSISI BAJA KARBON RENDAH HASIL PERLAKUAN NITRIDASI PLASMA DAN PELAPISAN DIAMOND LIKE CARBON. Penggunaan baja pada industri manufaktur khususnya baja karbon rendah sangat banyak ditemukan pada bahan komponen mesin maupun komponen konstruksi karena mempunyai sifat mudah dibentuk, tangguh dan murah. Kelemahan baja ini mempunyai sifat keras yang kurang baik sehingga tidak tahan aus dan menyebabkan umur pakai relatif pendek. Kelemahan ini dapat diselesaikan dengan peningkatan kekerasan yang dilakukan dengan perlakuan permukaan menggunakan metode nitridasi plasma diikuti pelapisan diamond like carbon (DLC) dengan variasi waktu dan suhu pada tekanan tetap sebesar 1,6 mbar. Proses nitridasi menggunakan gas nitrogen sedangkan pelapisan DLC menggunakan campuran gas CH4 dan Ar dengan perbandingan 24% : 76%. Hasil penelitian menunjukkan bahwa perlakuan permukaan dapat meningkatkan tingkat kekerasan pada permukaan dan merubah stuktur mikro serta komposisi. Berdasarkan hasil uji keras, proses nitridasi diikuti pelapisan DLC pada suhu 400 °C dengan waktu 5 jam nitridasi dan 1 jam pelapisan DLC diperoleh kekerasan sebesar 240,63 VHN, sedangkan kekerasan untuk waktu 5 jam nitridasi dan 1 jam pelapisan DLC pada suhu 450 °C sebesar 273,56 VHN. Adapun kekerasan raw material adalah 98,66 VHN. rn rnKata Kunci : diamond like carbon, nitridasi plasma, perlakuan permukaan. rnrnABTRAC ANALYSIS HARDNESS AND COMPOSITION LOW CARBON STEEL RESULTS OF PLASMA NITRIDING AND DIAMOND LIKE CARBON COATING. The use of steel in manufacturing industries, especially low carbon steel, is very much found in engine component materials and construction components because it has easy to form, tough and inexpensive properties. The weakness of this steel has poor hardness so it is not wear-resistant and causes a relatively short service life. This weakness can be solved by increasing the hardness done by surface treatment using the plasma nitriding method followed by coating of diamond like carbon (DLC) with a variation of time and temperature at a fixed pressure of 1.6 mbar. The nitriding process uses nitrogen gas while DLC coating uses a mixture of CH4 and Ar gas with a ratio of 24%: 76%. The results showed that surface treatment can increase the level of hardness on the surface and change the microstructure and composition. Based on the results of hard tests, the nitriding process was followed by coating the DLC at 400 ° C with 5 hours nitriding and 1 hour DLC coating obtained hardness of 240,63 VHN, while the hardness for 5 hours nitriding and 1 hour DLC coating at 450 ° C amounting to 273,56 VHN. The raw material hardness is 98.66 VHN. rnKeywords: diamond like carbon, plasma nitriding, surface treatment.

Ketersediaan
S19-023823/TA/M/19 669.112.2(043) YAN aPerpustakaan Poltek NuklirTersedia
Informasi Detail
Judul Seri
-
No. Panggil
669.112.2(043) YAN a
Penerbit
Yogyakarta : STTN-BATAN.,
Deskripsi Fisik
xvi, 52 halaman : ilustrasi ; 30 cm
Bahasa
Indonesia
ISBN/ISSN
-
Klasifikasi
669.112.2(043)
Tipe Isi
teks
Tipe Media
tanpa perantara
Tipe Pembawa
volume
Edisi
-
Subjek
-
Info Detail Spesifik
-
Pernyataan Tanggungjawab
Versi lain/terkait

Tidak tersedia versi lain

Lampiran Berkas
Komentar
Anda harus login sebelum memberikan komentar