Pengaruh implantasi ion nitrogen pada aluminium terhadap kekerasan, laju korosi, dan struktur kristal

PENGARUH IMPLANTASI ION NITROGEN PADA ALUMINIUM TERHADAP KEKERASAN, LAJU KOROSI, DAN STRUKTUR KRISTAL. Aluminium 5086 merupakan aluminium dengan kandungan magnesium yang banyak digunakan pada industri perkapalan, khususnya pada lambung kapal yang secara langsung bersentuhan dengan air laut. Untuk mengembangkan potensi aluminium maka telah dilakukan penelitian tentang pengaruh implantasi ion nitrogen pada aluminium 5086 terhadap kekerasan, laju korosi, dan struktur kristal. Implantasi ion dilakukan dengan energi 60 keV dan arus 75 µA. Waktu implantasi dilakukan selama 44 menit, 54 menit, 64 menit, 74 menit, dan 84 menit. Pengujian kekerasan dilakukan dengan metode Vickers, pengujian korosi dilakukan dengan metode elektrokimia, dan uji struktur kristal menggunakan X-ray Diffraction. Hasil dari penelitian ini adalah implantasi ion nitrogen pada waktu 54 menit mampu meningkatkan kekerasan sebesar 100,53% atau menjadi 37,5 VHN. Laju korosi pada kondisi implantasi ion nitrogen 54 menit adalah sebesar 0,011 mmpy atau menurun sebesar 8,3%. Terbentuknya fasa AlN ditunjukkan melalui puncak – puncak pada 2-theta sebesar 39,37°, 45,76°, dan 66,88° dengan bidang berturut – turut 111, 200, dan 202. rn rnKata kunci: Implantasi Ion, Aluminium, Kekerasan, Laju Korosi, Struktur Kristal rnrnABSTRACT rn rnEFFECT OF NITROGEN ION IMPLANTATION INTO ALUMINUM INTO AND THEIR SURFACE HARDNESS, CORROSION RATE, AND CRYSTAL STRUCTURE. Aluminum 5086 is an aluminum with magnesium as principal alloying element that widely used in marine application, especially on hull of the ships that directly in contact with sea water. In order to develop the potential of aluminum, the research have been done on the effect of nitrogen ion implantation on aluminum 5086 into surface hardness, corrosion rate, and crystal structure. Implantation of ions have done with energy 60 keV and current 75 μA. The duration of implantation was 44 minutes, 54 minutes, 64 minutes, 74 minutes, and 84 minutes. The surface hardness testing has done by Vickers Method, the corrosion testing has done by electrochemical method, and the crystal structure testing have done by using x-ray diffraction. The result of this research is nitrogen ion implantation at 54 minutes can increase surface hardness equal to 100,53% or become 37,5 VHN. The corrosion rate in the nitrogen ion implantation at 54 minutes 54 minutes is 0.011 mmpy or decreased by 8.3%. The AlN formation shown through the peaks at 2-theta was 39.37° (111), 45.76° (200), and 66.88° (202). rn rnKeywords: Ion Implantation, Aluminum, Surface Hardness, Corrosion Rate, Crystal Structure

Ketersediaan
S18-02046/TA/M/18 546.621(043) MUH pPerpustakaan Poltek NuklirTersedia
Informasi Detail
Judul Seri
-
No. Panggil
546.621(043) MUH p
Penerbit
Yogyakarta : STTN-BATAN.,
Deskripsi Fisik
xiii, 98 halaman : ilustrasi ; 30 cm
Bahasa
Indonesia
ISBN/ISSN
-
Klasifikasi
546.621(043)
Tipe Isi
teks
Tipe Media
tanpa perantara
Tipe Pembawa
volume
Edisi
-
Subjek
-
Info Detail Spesifik
-
Pernyataan Tanggungjawab
Versi lain/terkait

Tidak tersedia versi lain

Lampiran Berkas
Komentar
Anda harus login sebelum memberikan komentar