Sintesis dan karaterisasi silika mesopori SO₄²⁻/Al-KIT-5

Penelitian tentang sintesis dan karakterisasi silika mesopori SO42-/AL-KIT-5 telah dilakukan. Tujuan penelitian ini adalah menentukan pengaruh suhu sintesis dan waktu aging hidrotermal silika mesopori KIT-5 termodifikasi alumina (Al-KIT-5) terhadap luas permukaan spesifik, serta mengetahui karakteristiknya. Silika KIT-5 termodifikasi alumina disintesis pada suhu 30, 40, 50 dan 60 °C proses aging pada suhu 100 °C dengan waktu 6, 12, 18 dan 24 jam. Sulfonasi pada Al-KIT-5 menggunakan H2SO4. X-ray Diffraction (XRD), X-ray Fluoroscence (XRF), Fourier Transform Infrared (FTIR) dan Surface Area Analyzer (SAA) digunakan untuk mengkarakterisasi sampel hasil sintesis. Luas permukaan spesifik silika ditentukan dengan metode metilen biru dan BET. Hasil penelitian menunjukan bahwa luas permukaan spesifik tertinggi terbentuk pada suhu sintesis 60 °C dengan waktu aging 24 jam. Hasil karakterisasi pada keadaan optimum menunjukkan luas permukaan spesifik sebesar 843,53 m2/g dan luas permukaan spesifik setelah sulfonasi adalah 280,338 m2/g. Hasil karakteisasi XRF menunjukkan material mengandung Si, Al dan sulfat. Spektra FTIR menunjukan silika KIT-5 berhasil termodifikasi alumina. Data XRD memperlihatkan material berfasa amorf.
Kata kunci: Suhu sintesis, waktu aging, Al-KIT-5, sulfonasi

The research to synthesis and characterize mesoporous silica SO42/AL-KIT-5 is already conducted. The aim of this research is to determine the effect of the temperature and hydrotermal aging of alumina-modified mesoporous silica KIT-5 (Al-KIT-5) through the surface area and it charateristics. Alumina-modified silica KIT-5 was synthesized at temperatures of 30, 40, 50 and 60 °C, aging process in temperature of 100 °C for 6, 12, 18 and 24 hours. Sulfonation of Al-KIT-5 using H2SO4. X-ray Diffraction (XRD), X-ray Fluoroscence (XRF), Fourier Transform Infrared (FTIR) and Surface Area Analyzer (SAA) are used to characterize the synthesized material. The surface area is determined by methylene blue and BET methods. The results showed that the highest surface area of Al-KIT-5 silica is occurred at temperature of synthesize of 60 °C and an aged for 24 hours. The characterization results of Al-KIT-5 shows the optimum surface area is 843.53 m2/g and the surface area after sulfonation was 280.338 m2/g. The XRF characterization results showed that the material contained Si, Al and sulphate. FTIR spectra showed that KIT-5 was successfully modified aluminum. XRD data show that the material is amorphous.
Keywords: Synthesis temperature, aging time, Al-KIT-5, sulfonation

Ketersediaan
S18-01391/TA/H/18 631.41(043) AFR sPerpustakaan Poltek NuklirTersedia
Informasi Detail
Judul Seri
-
No. Panggil
631.41(043) AFR s
Penerbit
Yogyakarta : STTN-BATAN.,
Deskripsi Fisik
xiii, 57 halaman : ilustrasi ; 30 cm
Bahasa
Indonesia
ISBN/ISSN
-
Klasifikasi
631.41(043)
Tipe Isi
teks
Tipe Media
tanpa perantara
Tipe Pembawa
volume
Edisi
-
Subjek
-
Info Detail Spesifik
-
Pernyataan Tanggungjawab
Versi lain/terkait

Tidak tersedia versi lain

Lampiran Berkas
Komentar
Anda harus login sebelum memberikan komentar